home / Metallic polymers / Chester Metal Ceramic F

For complete technical information on this product consult the Technical Data Sheet (TDS):

Ceramic F

For safety information consult the Material Safety Data Sheet (MSDS):

en msds CeramicFFSL



Typical Industrial Applications (TIS):

Centrifuge work-area protection from chemical interaction (055)
Pump protection from chemical interaction and erosion (056)
Sealing up working transformer tank (086)
Placing bearing on damaged journal (090)
Vacuum pump regeneration (131)
TIS 17
Horizontal pulp regeneration and protection from erosion (159)
Pump's rotor reconstruction (168)
Repairing reinforced concrete container cracks (199)
TIS 25


Chester Metal Ceramic F


Chester Metal Ceramic F is a two-component molecular metal in a liquid form.

Application fields
  • regeneration of worn-out pump bodies and pump rotors
  • regeneration of worn-out propeller screws of ships and surfaces of rudder blades
  • regeneration of inner surfaces of pipes and valves surfaces
  • parts exposed to erosion and cavitation
Consistency
thixotropic paste
Mixing proportions: (Base : Reactor)
weight
volume


9:1
Maximal utility time after mixing (in 20°C)
15 min
Time for the mechanical working (in 20°C)
3.5 hours
Full chemical resistance (in 20°C)
after 7 days
Maximal working temperature
150°C
Bending temperature (DIN53462)
88°C
Compressive strength (ISO 604)
120 MPa
Bending strength (ISO 178)
110 MPa
Shear strength for steel base (ISO 4587)
14,9 MPa
Impact strength (ISO 179)
5,5 kJ/m2
Density
1.90 g/cm3
Package size
0.5 kg, 1 kg
Shelf life
3 years