Chester Metal Ceramic T

Chester Metal Ceramic T a molecular two-component thixotropic paste.

Application fields
  • regeneration of worn-out pump bodies and rotors
  • regeneration of worn-out propeller screws of ships
  • regeneration of worn-out surfaces of rudder blades and inner surfaces of pipes
  • regeneration of worn-out valves surfaces and gate valves surfaces
  • regeneration of parts exposed to erosion and cavitation
Consistency
thixotropic paste
Mixing proportions: (Base : Reactor)
weight
volume

2.5:1
2:1
Maximal utility time after mixing (in 20°C)
20 min
Time for the mechanical working (in 20°C
3.5 hours
Full chemical resistance (in 20°C)
after 7 days
Maximal working temperature
150°C
Bending temperature (DIN53462)
91°C
Compressive strength (ISO 604)
144 MPa
Bending strength (ISO 178)
90 MPa
Shear strength for steel base (ISO 4587)
15,8 MPa
Impact strength (ISO 179)
6,6 kJ/m2
Density
2.03 g/cm3
Package size
1 kg, 2 kg
Shelf life
3 years