Chester Metal Super SL Chester Metal Super SL is the most popular used molecular two-component thixotropic paste.
Application fields:
- repairing leaks in the central heating lines
- reconditioning of the worn-out bearing mountings and the worn-out anti-friction bearing journals
- repair of leaks in tanks, cracked frames or bodies, e.g. engine block or leaks in welds of any kind
- reconditioning of stripped threads and worn-out splineways
- correction and sealing the iron or steel and nonferrous castings
- bridge bearings setting
- reconditioning of corroded of heat exchanger bottoms and fixings of parts in metal, concrete, etc.
|
Consistency
|
thixotropic paste
|
Mixing proportions: (Base : Reactor)
weight
volume |
2.3:1
2:1
|
| Maximal utility time after mixing (in 20°C) |
90 min
|
| Time for the mechanical working (in 20°C) |
8 hours
|
| Full chemical resistance (in 20°C) |
after 7 days
|
| Maximal working temperature |
150°C
|
| Bending temperature (DIN53462) |
90°C
|
| Compressive strength (ISO 604) |
146 MPa
|
| Flexural strenght (ISO 178) |
90 MPa
|
| Shear strength for steel base (ISO 4587) |
20.4 MPa
|
| Impact strength (ISO 179) |
5.4 kJ/m2
|
| Density |
2,23 g/cm3
|
| Package size |
0.5 kg, 1 kg, 2 kg, 5 kg
|